DURASTAT® - STATIC DISSIPATIVE CONCENTRATES

Product Selector

Product	Mil SPec B-81705C	Non-Amine	Blown & Caat Film	Extrusion & Coextrusion	Injection Molding	High Thermal Stability	Antiblock	Flame Retardant
POLYETHYLENE - STATIC DISSIPATIVE
LD-100	•	•	•	•		•
LD-120	•	•	•	•		•	•
LD-200	•	•			•	•
POLYETHYLENE - STATIC DISSIPATIVE / FLAME RETARDANT
AS-5903-3	•	•	•	•	•			•

PMC Group, inc. and Polymer Products Company, Inc. do not warrant the applicability of these products in any end-use applications. Customers must determine the suitability of any product in their application.

Typical Properties

Property	Units	Test Method	LD-100*	LD-120*	LD-200*	AS-5903-3**
Specific Gravity	g/cm2	ASTM-D-792	1.02	1.02	1.02	1.87
Electrostatic Decay	sec.	Mil-Spec B-81705C	0.6	0.6	0.5	0.74
Surface Resistivity	Ohms/sq	ASTM D-257	<10¹²	<10¹²	<10¹²	1.6x10¹¹
Typical Letdown for Mil Spec B-81705-C	%	PPC Method	4-6	4-6	5-10	10-28
Flame Retardancy		NFPA-701	N/A	N/A	N/A	Pass
Surface Flammability		ASTM D-162	N/A	N/A	N/A	Pass
Flame Spread, Smoke, Optical Density		ASTM D-662	N/A	N/A	N/A	Pass

* Values obtained after 48 hours at 12% relative humidity on 2 mil LDPE film with a 6% concentration of Durastat®.
** Values obtained after 48 hours at 12% relative humidity with a 14% concentration of Durastat® AS-5903-3 in LDPE.

Polycarbonate Stress Performance

Durastat Product	Units	Film Thickness	Loading	73°F	120°F	158°F	185°F
LD-100	psi	2 mil	3%	>3400	>3400	1700	1700
LD-120	psi	2 mil	4%	>3400	>3400	1700	1700
LD-200	psi	5 mil	6%	>3400	>3400	1700	1700